On November 11, 2015, Liang, Ruiyong; Gao, Hai published a patent.COA of Formula: C17H24N4O6 The title of the patent was An aqueous environmentally-friendly abrasion resistant coating. And the patent contained the following:
The title coating is prepared from alkyd resin 90-100, 1, 2- dimethoxyethane 1-2, aluminum borate whisker 3-5, volcanic ash 1-2, expanded perlite 3-4, polyvinyl alc. 2-3, dimethylaminopropylamine 0. 6-1, calcium naphthenate 0. 5-1, isooctyl methacrylate 2-4, magnesium stearate 1-3, manganese sulfate 0. 5-1, aluminum sulfate 1-2, stearic acid 0. 7-1, wollastonite powder 8-12, flame retardant additive 2-4, STPP 1-2, and deionized water 80-100 weight parts. The title coating is produced by mixing volcanic ash, expanded perlite and wollastonite powder, ball milling uniformly to obtain the grinding material; adding STPP into water, stirring uniformly, adding stearic acid and calcium naphthenate, stirring at 30-40 °C for 5-7 min to obtain the activation solution; adding the grinding material into the activation solution, stirring uniformly, adding dimethylaminopropylamine, stirring and dispersing at 100-200 rpm for 20-30 min to obtain the pre-mixture; mixing polyvinyl alc., Mn sulfate and Al sulfate, stirring and mixing at 50-60 °C for 3-5 min, adding above pre-mixture, stirring uniformly, adding 1,2-dimethoxyethane, the left deionized water and alkyd resin, stirring and dispersing at 300-400 rpm for 1-2 h, mixing with the left raw materials, stirring and dispersing at 600-1000 rpm for 20-30 min to obtain the title coating product. The experimental process involved the reaction of 5-(3,4,5-Trimethoxybenzyl)pyrimidine-2,4-diamine 2-hydroxypropanoate(cas: 23256-42-0).COA of Formula: C17H24N4O6
The Article related to alkyd resin abrasion resistant coating, Coatings, Inks, and Related Products: Polyester and Alkyd Resin Coatings and other aspects.COA of Formula: C17H24N4O6
Referemce:
Pyrimidine | C4H4N2 – PubChem,
Pyrimidine – Wikipedia